Mohammed S. Bin-Shuwaish

Department of Restorative Dental Sciences, College of Dentistry, King Saud University- P. O. Box 60169, Riyadh 11545 Kingdom of Saudi Arabia

Corresponding author email: shuwaishmo@gmail.com

Article Publishing History

Received: 05/01/2020

Accepted After Revision: 10/03/2020

ABSTRACT:

The aim of the study was to evaluate the adhesive bond strength of Bioactive cements to lithium disilicate ceramics in comparison to the resin based luting cements with two surface treatments, hydrofluoric acid (HF) and Er Cr YSGG laser (ECL). Ninety specimens ceramic disks were fabricated and divided into three groups (n=30) based on the surface treatment employed; HF, ECL for 2minute duration and ECL for 4 minute duration. The laser treated groups were prepared with the use of a gold handpiece using an MZ10 tip size (Er Cr: YSGG, water lase I plus).  Surface treated disks in each were further divided into three sub groups (n= 10) based on the type of cement applied; Bioactive cements, Rely X unicem and Rely X ARC. Subsequent to the application of the cements, bulk fill composite was build up with the help of the putty mould; specimens were placed in a thermocycler for 5000 cycles at 50C and 550C. Each specimen disk was tested under the universal testing machine for shear bond strength (SBS). Data was analysed using analysis of variance and Tukey’s – Kramer multiple tests (p<0.05). The maximum mean value for shear bond strength achieved was 23.55 (±2.26) for Rely-x unicem­-HF-S and the minimum mean value was 14.30 (±2.08) for the group bioactive and ECL-2. Therefore, it was concluded that the adhesive bond strength of the bioactive cements on lithum disilicate ceramics was lower than the resin based luting cements. Difference in surface treatments did not influence the adhesive bond strength of bioactive cements to the lithium disilicate ceramic.

KEYWORDS:

Lithium Disilicate, Er Cr YSGG Lasers, Self Etch Resin Luting Agents, Rely X and Bioactive Cements.

Download this article as:

Copy the following to cite this article:

Bin-Shuwaish M. S. Adhesive Bond Strength of Bioactive Cement to Er Cr YSGG Laser Treated Lithium Disilicate Ceramics. Biosc.Biotech.Res.Comm. 2020;13(1).


Copy the following to cite this URL:

Bin-Shuwaish M. S. Adhesive Bond Strength of Bioactive Cement to Er Cr YSGG Laser Treated Lithium Disilicate Ceramics. Biosc.Biotech.Res.Comm. 2020;13(1). Available from: https://bit.ly/38Id9oI


INTRODUCTION

The most popular technology that has become the centre of choice in dental restoration recently is all ceramic restorations (Zarone et al., 2016). These restorations offer a series of advantage over the metal porcelain used, such as biocompatibility, low thermal conductivity, high optical properties, better chemical stability and comparable coefficients of thermal expansion to the teeth (Niu et al., 2014, Niu et al., 2013, Aboushelib and Sleem, 2014). Lithium disilicate (LD) is the most common type of contemporary adhesive glass ceramics employed in modern dentistry (Elsayed et al., 2017). In Comparison to zirconia, lithium disilicate ceramics are processed through the hot press technique exhibiting greater potential for restoration displaying translucency and aesthetics (Palla et al., 2018). The lithium silicate ceramics comprise of silica glass matrix and lithium oxide (Li2O) that presents greater flexural strength compared to the leucite-reinforced glass ceramics (Klosa et al., 2013). The crystals in the lithium disilicate ceramic are the unit of foundation that offers better mechanical strength to the ceramics such as fracture toughness, chemical durability and abrasion resistance (Lee et al., 2017).

Efforts have been made in formulating a resin based luting agent with improved mechanical strength, toughness and fracture resistance (Koizumi et al., 2012). These bioactive cements have demonstrated improved and better functional properties critical for clinical function and survival. The volumetric shrinkage of these materials is <1.7% compared to the resin based composites (Al-Sowygh, 2017). These materials have successfully presented with properties equivalent to glass ionomer including intimate contact with the dentin walls and display hydrophilicity (Pekkan and Oezcan, 2012). Studies have pointed out that the adhesive bond between the ceramic restoration and the cement is the main factor for fracture resistance and marginal adaptation rather than the strength of the ceramic (Özcan and Mese, 2012, Koizumi et al., 2012).

Few authors have employed different surface treatments for stronger adhesive bond strength between LD ceramics and bioactive cements through increasing surface roughness (Bagis et al., 2011, Al-Sowygh, 2017). According to Koizumi et al. (2012), sandblasting reported serious damage to the ceramic surface resulting in low flexural strength; however, hydrofluoric surface treatment chemically modified the surface creating irregular interlocking surface. This technique improved interfacial bonding through an increase in the bonding area. In many instances, clinicians have applied silane coupling agent to decrease the wettability contact angle and increase the free energy of the ceramic surface (Koizumi et al., 2012, Al-Sowygh, 2017).

Recently, the use of lasers in modern dentistry has led to increased beneficial effects in terms of painless removal of infected dentine and long term retention of the restoration. Er Cr YSGG (ECL) laser working is based on micro explosion creating surface irregularities for micro retention, which is considered favourable surface treatment compared to hydrofluoric acid that has the tendency to ablate the tissue in process of etching surface. Hence, using hydrofluoric acid on the chairside is risky for the patient, (Kursoglu et al., 2013, Vohra et al., 2019).

In the current view, the self-etched resin had replaced the conventional bonding technique of the glass ceramics using the resin based luting agents (Yilmaz-Savas et al., 2016). Self etch agents such as Rely X unicem are commonly employed as bonding cement in ceramic restoration. The recent introduction of Bioactive cements with inherent beneficial properties such as an efficient dentinal bond, resin tag supported adhesion, caries resistance, continuous fluoride release, dentin formation, and pulp protection compels to opt as a luting agent in the ceramic restoration (Al-Sowygh, 2017, Chaharom et al., 2018).

Therefore, it is hypothesized Bioactive cements would show higher adhesive bond strength in Er Cr YSGG laser treated disilicate glass ceramics. Literature provides series of studies comparing the self etch and conventional luting agents bond strength in ceramics; however, there is no plausible data for displaying the adhesive bond strength in regards to bioactive cements in ceramic under different surface treatment (Yaman et al., 2014, Aguiar et al., 2014). Thus, the present study intends to evaluate the adhesive bond strength of bioactive cements in Lithium disilicate ceramics under two surface treatment; hydrofluoric acid and Er Cr YSGG treatment in comparison to the resin based luting agents.

MATERIALS AND METHODS

The present in vitro study evaluated the adhesive bond strength of Bioactive cement to Er-Cr-YSGG laser treated Lithium disilicate ceramics. Under the heat pressed technique, a total of 90 lithium silicate ceramic disks were fabricated (EMax Press, Ivoclar Vivadent, AG, Schaan/Liechtenstein MO1 lot no.10721) with height (Ø) and diameter of 3 mm x 3 mm, respectively. The materials details are provided in table 1.

To achieve a flat base, the ceramic disc was embedded into the acrylic resins with PVC (polyvinyl chloride) particles. The disks were finished through grinding under running water using silicon carbide paper on a polishing machine (Buehler Polishing Machine type: 49-5100-230, No 620-PXB-22061, Germany).  The 90 specimens were initially divided into three main groups (n= 30) followed by distribution into 3 groups in each category (n= 10) depending upon the surface treatment and the type of luting agent used, correspondingly.The group distribution according to the surface treatment is described as follows:

Group 1 HF -S (silane) (Control): the specimen’s surface was treated with the 9.6% concentration hydrofluoric acid (Pulpdent Corporation, USA). The etchant is applied for 1 min and washed along with air dried for 2 mins. Subsequently, after cleaning, silane adhesive (Silane bond enhancer, Pulpdent- Watertown, MA, USA) was smeared over the etched surface using a micro brush and allowed to dry for 5 mins.

Group 2 ECL-2:  the specimen’s surface was treated with Er Cr:YSGG laser (water lase I plus, Biolase, USA) at a power of 3.75W and frequency of 15 Hz (L1), air-water 90-70% for 2 mins. Followed by the application of silane adhesive with micro brush and allowing it to dry for 5 mins.

Group 3 ECL-4: a similar procedure as group 2 proceeded; however, the laser surface treatment prolonged for 4 mins. Moreover, the specimens in both the laser treated groups were prepared with the use of a gold handpiece using an MZ10 tip size (Er Cr:YSGG , water lase I plus, Biolase, USA). The focus of the handpiece was in the centre for 30 seconds followed by a standard clockwise rotational movement for the remaining time at distance 2 mm. Subsequently, each of the three groups was further divided according to the type of luting agent used. Group HF-S-Bioactive: Bonding with ACTIVA- Bioactive cement (Pulpdent- Watertown, MA, USA).

Group HF-S-Rely-X: Bonding with RelyX Unicem (3M, St. Paul, MN, USA)

Group HF-S-Rely-ARC: Bonding with RelyX-ARC (3M, St. Paul, MN, USA)

Group ECL-2-Bioactive: Bonding with ACTIVA- Bioactive cement

Group ECL-2-Rely-X: Bonding with RelyX Unicem , after complete procedure

Group ECL-2:Rely-ARC: RelyX-ARC (3M, St. Paul, MN, USA)

Group ECL-4-Bioactive: Bonding with ACTIVA- Bioactive cement

Group ECL-4-Rely-X: Bonding with RelyX Unicem

Group ECL-4:Rely-ARC: Bonding with RelyX-ARC (3M, St. Paul, MN, USA)

Following the preparation, each of the specimen disks was coated with either of three different types of the luting agent. The luting agents were polymerised using curing light (Bluephase®, Ivoclar Vivadent, Schaan, Liechtenstein) at a light intensity of 1,000 mW/cm2 for 10 seconds. Consequently, after complete preparation of the specimen, using a putty mould (Polyvinyl siloxane- Express, 3M Center St. Paul, MN, USA) the bulk-fill resin composite (Multicore flow, Ivoclar Vivadent) (Ø 2 mm, depth 2 mm) was build upon the specimen disk and polymerised from each side for 40 seconds in total. Each specimen was placed in thermocycler afterward (Thermocycler SD Mechatronik, GmbH Dental Research Equipment, Germany) for 5000 cycles at 50C and 550C (dwelling time: Cold bath, 30 sec; Hot bath, 30 sec).

Subsequent to thermocycling, the specimen from each group was placed under load in the universal testing machine (Instron 8500 Plus, 100 Royal St. Canton USA).  The chisel of the universal machine is placed on the specimen at a perpendicular direction at a control force rate of 1 mm/min until the build-up materials were detached from the ceramic surface. To examine the failure mode of the detached surface, the digital microscope (Hirox- KH7700) was used. The failures are observed at three levels: adhesive failure at the luting agent and ceramic interface, cohesive: failure within the cement or the ceramic or composite materials, and admixed: Failure at luting/ceramic interface, progressing into luting cement.

All the data collected for the adhesive bond strength was processed and tabulated using a statistical program for social science (SPSS). The analysis of normally distributed data was performed using Kolmogorov-Smirnov test. The shear bond strength was analysed using analysis of variance and Tukey’s – Kramer multiple tests (p<0.05). Furthermore, all data recorded was subjected to Levene’s test of homogeneity of variance (α= 0.05) following the assumption of equal variances.

Table 1. Details of the materials used in the study

Material Composition Details Filler
 

RelyX™ Unicem

3M, ESPE, St Paul, MN,USA

 

Methacrylated phosphoric ester

Dimethacrylate (TEGDMA, Bis-GMA), Stabiliser,

Peroxy compound, Substituted

pyrimidine  Pigment,

Calcium hydroxide

 

Barium glass, ytterbium
trifluoride, and mixed oxide

RelyX™ ARC

3M, ESPE, St Paul,

USA

TEGDMA, Bis-GMA,

Benzoic peroxide, amine, photo-initiator, pigment.

Barium-alumino-fluoro-borosilicate glass,
Strontium alumino-fluoro-silicate glass , Zirconia powder
ACTIVA BulkfillTM , Bio Active, ionic composite resin,

Pulpdent, Germany

Blend of diurethane and other methacrylates with modified polyacrylic acid (44.6%)

contain no Bisphenol  A, No Bis-GMA, No BPA derivatives

Amorphous silica (6.7%)

Sodium fluoride (0.75%)


RESULTS AND DISCUSSION

Kolmogorov-Smirnov test presented with normal distribution of data. The analysis of variance (ANOVA) displayed a significant difference in the adhesive bond strength of bioactive cement to Er Cr YSGG laser treated Lithium disilicate ceramics in comparison to the resin based luting cements (p=0.01). The outcome of the present study displayed significant difference (p<0.05) for the two different surface treatments employed in the bioactive cement group. Resin luting cements also presented significant difference with the two surface treatment; HF and Er Cr YSGG laser treatment employed (p<0.05).The present study demonstrated that the maximum mean value for adhesive shear bond strength was 23.55 (±2.26) for the group Rely-x unicem ­- HF-S and the minimum mean value was 14.30 (±2.08) for the group bioactive cement-ECL-2. The means and standard deviations of bond strength obtained are summarized in table 2.

Table 2. Means and SD for shear bond strength among study groups

Luting agent HF-S ECL-2 ECL-4 P value
Bioactive (Activa) 17. 45 (2.40)a A 14.30 (2.08)b B 17.37 (2.23) a A  

< 0.01

RelyX- Unicem 23.55 (2.26)b  A 16.37(3.11)ab B 18.40 (2.61)ab B
Rely-X ARC 21.37 (2.38)b A 18.33 (2.83)a B 20.65 (2.76)b  AB

Dissimilar superscript small alphabets in same column show significant difference (p< 0.05)

Dissimilar superscript capital alphabets in same row show significant difference (p< 0.05)

Each luting agent used in the study presented with a different set of bond strength mean value varying according to the employed surface treatments, respectively. Comparing the luting agent outcomes indicated an evident difference in shear bond strength of Activa and Relyx cements (unicem and ARC) (p < 0.01). The surface prepared with the silanised process (HF-S) specifically produced better shear bond strength results. Multiple comparisons test demonstrated a significant difference between the bioactive and Relyx cements (unicem and ARC) only under the hydrofluoric – silane surface treatment. In contrast, the laser treated surface (ECL-2 and ECL-4) presented with an evident difference between bioactive and Rely – ARC cement whereas exhibiting comparable results between the Activa and Rely Unicem. Despite the fact there was a significant difference in the result; nevertheless, Bioactive cements presented with lower bond strength compared to the resin luting agents.

Analysing the effect of the surface treatment on the each material, the result of bioactive cements presented a significant difference between the two laser groups [ECL-2 (14.30 (2.08), ECL-4 (17.37 (2.23)] and HF-S group (17. 45 (2.40)) with ECL-2 (14.30 (2.08)) respectively. Whereas comparable outcome was observed between the HF-S and ECL -4 groups (p >0.05). Rely-x cements (unicem and ARC) showed an evident difference between the HF-S and laser treated group (ECL-2); however, Rely X unicem presented similar results between the two types of laser treatment. In addition, a significant difference was observed between the HF-S and laser treated group (ECL-4) in Rely X unicem while no significant difference in Rely X ARC. Thus, Bioactive cements showed an insignificant difference in adhesive bond strength in Er-Cr-YSGG treated lithium disilicate compared to the HF-S group.

Table 3. Failure type percentage among study groups

Study Groups Adhesive Cohesive Mixed
Group HF-S-Bioactive 70 0 30
Group HF-S-Rely-ARC 80 0 20
Group HF-S-Rely-ARC 80 0 20
Group ECL-2-Bioactive 100 0 0
Group ECL-2-Rely X 70 0 30
Group ECL-2-Rely-ARC 80 0 20
Group ECL-4-Bioactive 70 0 30
Group ECL-4-Rely X 70 0 30
Group ECL-4-Rely-ARC 60 0 40

Failure mode outcomes exhibited adhesive failure in the majority of the specimens compared to cohesive and admixed failures. The result indicated that only specimens in ECL-2 group presented in Bioactive material showed 100% adhesive failure. Overall, only 20 – 30% of observed failures were admixed type. The results directed that the ECL-2 had a profound effect on the shear bond strength of bioactive cement compared to Rely X cements. These Rely X cements in between them demonstrated a comparable number of failures in each surface treatment. However, ECL- 4 treatment did not show an apparent difference in the type of failure among either cement.

The present study evaluates the adhesive bond strength of bioactive cement to Er-Cr-YSGG laser treated lithium disilicate ceramics based on the hypothesis that bioactive cements exhibit better adhesive bond strength compared to self etch resin based luting agents. The study compared bonding strength of bioactive cements under hydrofluoric acid and Er Cr YSGG surface treatment for 2 and 4 minute duration. Self etched resin cements (Rely X unicem) demonstrated higher bond strength compared to the bioactive cements. Furthermore, under different surface treatments bioactive cements showed significant change in shear bond strength to LD ceramics. Therefore the hypothesis was rejected. A multitude of explanations can be provided for the outcomes in the present study.

To maintain the homogeneity and standardisation the adhesive shear bond strength was assessed using a universal testing machine. All the specimens were thermocycled to ensure the shear bond strength tested was in a standard environment. Studies have reported that thermocycling determines a positive change in surface bonding, which has beneficial long term effects on the ceramic restoration (Brum et al., 2011, Lee et al., 2017). Thermocycling aids in the water resorption property that causes the ageing of the bond resulting in weak bonds (Brum et al., 2011). The bioactive cements in previous studies have demonstrated an insignificant decrease in adhesive bond strength to ceramics compared to resin based luting cement despite the fact some detrimental effects are associated with water resorption due to the methacrylate in resin cements (Brum et al., 2011, Ahrari et al., 2017).

In the present study, Rely X cements showed higher bond strength compared to the bioactive cements. Rely X unicem (self etched) displayed higher mean value in HF surface treatment while Rely X ARC (resin based) displayed high mean value in laser treated group. Nevertheless, comparable bond strength was observed between the self etch and resin cements. The results of the present study partially supported the outcomes noted by the previous studies regarding higher bond strength in the self etch cements and lower bond strength in bioactive cements (Al-Sowygh, 2017). The plausible explanation identified was that self etch cements uses dual cure method to polymerise; therefore, presented with better bond strength (Chaharom et al., 2018).

The lower bond strength of the bioactive cements suggested that the durability of the bond depends upon the nature of the mechanical bond between the ceramics and cements (Gurney et al., 2016). As ceramics are inert in nature they do not display chemical change that would contribute to the bonding strength (Kursoglu et al., 2013). In addition, theoretically, the silane bond on the ceramic surface binds effectively to the micro retentive etched surface.  However, the bioactive cements offer limited methacrylate group for bonding to the silane groups compared to resin based cements; thus, resulting in low bond strength (Ahrari et al., 2017, Al-Sowygh, 2017).

Several studies documented the evident effect of hydrofluoric acid on the interfacial bonding surface(Lee et al., 2017, Kalavacharla et al., 2015). Whereas few previous studies used different intensity laser application to identify the effect on the ceramic surface (Passia et al., 2015, Kalavacharla et al., 2015). Therefore, to observe the evident effect of the varying surface treatment on the ceramic surface, two types of surface treatments were employed HF-S and Er Cr YSGG laser treatment. In the present study, the duration of the laser was varied in order to observe the effect on the adhesive bond strength to lithium disilicate ceramics. It is reported that laser treated surface often displays greater surface roughness irregularities and patterns, unlike the HF that dissolves the ceramics glassy matrix to form interlocking surface (Neis et al., 2015). The interlock mechanism implicates better micromechanical retention compared to an irregular surface. Intriguingly, a prolonged period of laser application increase surface roughness; nevertheless, the laser produces excessive heat that results in the weakening and over destruction of the surface (Gurney et al., 2016). Hence, laser treated ceramics with prolonged duration demonstrated higher bond strengths but comparatively less than the HF study groups.

The mode of failure assessment presented a higher number of adhesive failures followed by admixed. No specimen demonstrated cohesive failure in the present study attesting no measurement of material strength. The bioactive cements displayed an increased number of adhesive failure only in ECL 2 group while comparable results were appreciated in other groups. This indicates employing bioactive cements at laser treated surface with 2 min duration results in the formation of weak adhesive bonds comparatively to laser treated surface at 4 min duration. Nevertheless, failure mode assessment displayed comparable adhesive bond strength of bioactive cements and resin luting cements.

Certain limitations were identified in the present study despite the fact it provided a clear comparison between the bioactive cements and resin based luting agents. The results of the study are applicable only in reference to the particular surface treatments employed, particularly the type of laser (Er Cr YSGG) used. For better understanding of the bonding strength of bioactive cements to ceramics, studies comparing different types of ceramics that are recommended. Although the study presented lower bond strength of bioactive cements to the ceramics; however, the status of fracture resistance of bioactive cements is questionable and that needs to be evaluated. Lithium disilicate ceramics are well established restoration used in dentistry exhibiting inherent properties necessary for efficient adhesive bonding and long term retentive restoration. The mechanical and biological properties of Bioactive cements shows great potential in bonding with the tooth; however, literature provides limited data with respect to its bonding with the ceramics. Therefore it is recommended to evaluate the fracture resistance of these Biocements prior to the application of different laser with different types of ceramic restorations.

CONCLUSION

The adhesive bond strength of the bioactive cements to lithum disilicate ceramics was lower than the resin based luting cements. Use of 4 minutes of Er Cr YSGG laser treatment displayed an increase in the adhesive bond strength of bioactive cement to Lithium disilicate ceramics. Despite the low bond strength, Bioactive-luting agents exhibited durable bond strength to the ceramics.

REFERENCES

Aboushelib, M. N. and Sleem, D. (2014). Microtensile Bond Strength Of Lithium Disilicate Ceramics To Resin Adhesives. J Adhes Dent, 16(6):547-52.

Aguiar, T. R., André, C. B., Correr-Sobrinho, L., Arrais, C. A., Ambrosano, G. M. and Giannini, M. (2014). Effect Of Storage Times And Mechanical Load Cycling On Dentin Bond Strength Of Conventional And Self-Adhesive Resin Luting Cements. The Journal Of Prosthetic Dentistry, 111(5):404-10.

Ahrari, F., Boruziniat, A., Mohammadipour, H. S. and Alirezaei, M. (2017). The Effect Of Surface Treatment With A Fractional Carbon Dioxide Laser On Shear Bond Strength Of Resin Cement To A Lithium Disilicate-Based Ceramic. Dental Research Journal, 14(3):195.

Al-Sowygh, Z. H. (2017). Bond Strength Of Novel Bioactive Resin Modified Luting Agent To Lithium Disilicate Dental Ceramic. Journal Of Biomaterials And Tissue Engineering, 7(12):1349-54.

Bagis, B., Bagis, Y. H. and Hasanreisoğlu, U. (2011). Bonding Effectiveness Of A Self-Adhesive Resin-Based Luting Cement To Dentin After Provisional Cement Contamination. Journal Of Adhesive Dentistry, 13(6).

Brum, R., Mazur, R., Almeida, J., Borges, G. and Caldas, D. (2011). The Influence Of Surface Standardization Of Lithium Disilicate Glass Ceramic On Bond Strength To A Dual Resin Cement. Operative Dentistry, 36(5):478-85.

Chaharom, M. E. E., Azar, F. P., Mohammadi, N. and Nasiri, R. (2018). Effect Of Surface Preparation With Nd: Yag And Er, Cr: Ysgg Lasers On The Repair Bond Strength Of Lithium Disilicate Glass Ceramic To A Silorane-Based Composite Resin. Journal Of Dental Research, Dental Clinics, Dental Prospects, 12(1):12.

Elsayed, A., Younes, F., Lehmann, F. and Kern, M.(2017). Tensile Bond Strength Of So-Called Universal Primers And Universal Multimode Adhesives To Zirconia And Lithium Disilicate Ceramics. J Adhes Dent, 19(3):221-8.

Gurney, M. L., Sharples, S. D., Phillips, W. B. and Lee, D. J. (2016). Using An Er, Cr: Ysgg Laser To Remove Lithium Disilicate Restorations: A Pilot Study. The Journal Of Prosthetic Dentistry, 115(1):90-4.

Kalavacharla, V. K., Lawson, N., Ramp, L. and Burgess, J. (2015). Influence Of Etching Protocol And Silane Treatment With A Universal Adhesive On Lithium Disilicate Bond Strength. Operative Dentistry, 40(4):372-8.

Klosa, K., Boesch, I. and Kem, M. (2013) Long-Term Bond Of Glass Ceramic And Resin Cement: Evaluation Of Titanium Tetrafluoride As An Alternative Etching Agent For Lithium Disilicate Ceramics. Journal Of Adhesive Dentistry, 15(4).

Koizumi, H., Nakayama, D., Komine, F., Blatz, M. B. and Matsumura, H. (2012). Bonding Of Resin-Based Luting Cements To Zirconia With And Without The Use Of Ceramic Priming Agents. Journal Of Adhesive Dentistry, 14(4).

Kursoglu, P., Motro, P. F. K. and Yurdaguven, H. (2013). Shear Bond Strength Of Resin Cement To An Acid Etched And A Laser Irradiated Ceramic Surface. The Journal Of Advanced Prosthodontics, 5(2):98-103.

Lee, H.-Y., Han, G.-J., Chang, J. and Son, H.-H. (2017). Bonding Of The Silane Containing Multi-Mode Universal Adhesive For Lithium Disilicate Ceramics. Restorative Dentistry and Endodontics, 42(2):95-104.

Neis, C. A., Albuquerque, N. L. G., Albuquerque, I. D. S., Gomes, E. A., Souza-Filho, C. B. D., Feitosa, V. P., Spazzin, A. O. and Bacchi, A. (2015). Surface Treatments For Repair Of Feldspathic, Leucite-And Lithium Disilicate-Reinforced Glass Ceramics Using Composite Resin. Brazilian Dental Journal, 26(2):152-5.

Niu, E., Agustin, M. and Douglas, R. D. (2013). Color Match Of Machinable Lithium Disilicate Ceramics: Effects Of Foundation Restoration. The Journal Of Prosthetic Dentistry, 110(6):501-9.

Niu, E., Agustin, M. and Douglas, R. D. (2014). Color Match Of Machinable Lithium Disilicate Ceramics: Effects Of Cement Color And Thickness. The Journal Of Prosthetic Dentistry, 111(1):42-50.

Özcan, M. and Mese, A. (2012). Adhesion Of Conventional And Simplified Resin-Based Luting Cements To Superficial And Deep Dentin. Clinical Oral Investigations, 16(4):1081-8.

Palla, E.-S., Kontonasaki, E., Kantiranis, N., Papadopoulou, L., Zorba, T., Paraskevopoulos, K. M. and Koidis, P. (2018). Color Stability Of Lithium Disilicate Ceramics After Aging And Immersion In Common Beverages. The Journal Of Prosthetic Dentistry, 119(4):632-42.

Passia, N., Lehmann, F., Freitag-Wolf, S. and Kern, M. (2015). Tensile Bond Strength Of Different Universal Adhesive Systems To Lithium Disilicate Ceramic. The Journal Of The American Dental Association, 146(10):729-34.

Pekkan, G. and Oezcan, M. (2012). Radiopacity Of Different Resin-Based And Conventional Luting Cements Compared To Human And Bovine Teeth. Dental Materials Journal, 1201190225.

Vohra, F., Labban, N., Al-Hussaini, A., Al-Jarboua, M., Zawawi, R., Alrahlah, A. and Naseem, M. (2019). Influence Of Er; Cr: Ysgg Laser On Shear Bond Strength And Color Stability Of Lithium Disilicate Ceramics: An In Vitro Study. Photobiomodulation, Photomedicine, And Laser Surgery, 37(8):483-8.

Yaman, B. C., Ozer, F., Takeichi, T., Karabucak, B., Koray, F. and Blatz, M. B. (2014). Effect Of Thermomechanical Aging On Bond Strength And Interface Morphology Of Glass Fiber And Zirconia Posts Bonded With A Self-Etch Adhesive And A Self-Adhesive Resin Cement To Natural Teeth. The Journal Of Prosthetic Dentistry, 112(3):455-64..

Yilmaz-Savas, T., Demir, N., Ozturk, A. N. and Kilic, H. S. (2016). Effect Of Different Surface Treatments On The Bond Strength Of Lithium Disilicate Ceramic To The Zirconia Core. Photomedicine And Laser Surgery, 34(6):236-43.

Zarone, F., Ferrari, M., Mangano, F. G., Leone, R. and Sorrentino, R. (2016). Digitally Oriented Materials: Focus On Lithium Disilicate Ceramics. International Journal Of Dentistry, 2016.